E71-T1 SAW
Flux Cored Wires
1.6, 2, 2.4, 2.8mm
Brand: CIGWELD

Hardfacing SAW
Flux Cored Wires
55-63 HRC, 2.8mm
Brand: Cobalarc

Welding Electrode
18-8-6, 5mm
Brand: WeldKraft

ER CuSi-A
MIG Wire, 0.9mm
Brand: National(USA)

Cr-Mo TIG Wires
All Sizes
Brand: Gedik/Kobelco

Inconel Electrodes
NiCrFe-3, NiCrFe-4,
NiCrFe-9
3.2mm, 4mm,
Brand: Kobelco

Call for special price at: +91-9810654634
Welding Electrodes : Mild Steel
Grade Characteristic
E6010
Element C Mn Si
Percent 0.07 0.50 0.20
E6010 is ideally suited for welding in all positions including vertical down. Ideal for stove pipe technique and faster welding. Welds are of radiographic quality. Typical applications include welding of Pipes, tubes,  and ducts etc.
E6013
Element C Mn Si
Percent 0.08 0.44 0.22
A medium rutile type all position electrode for welding  mild steel  structures, rail coaches, wagons,  storage tanks, ships, sheet metal work etc.
E7010
Element C Mn Si S P Mo
Percent 0.08 0.45 0.15 0.02 0.025 00.51
This electrode is a light coated cellulosic type electrode. This electrode operates with a penetrating arc. Ideally suited for welding in all positions including vertical down. Special feature has been found extremely beneficial  for welding  of pipes  in “Stove Pipe technique” both for faster  welding and greater control on penetration of the root runs.
E7018
Element C Mn Si
Percent 0.06 1.02 0.44
A heavy coated low hydrogen, iron powder type electrode ideally suited for  producing tough and ductile welds of radiographic quality in boilers, pressure vessels, and heavy structures subjected to dynamic loading. The electrodes have a metal recovery of about  115%. Some typical applications  include  heavy  structures  subjected to  dynamic loading  and impact, highly restrained joints, coaches,  wagons, penstocks, boilers,  pressure vessels, earthmoving machines etc.
E8018
Element C Mn Si Ni
Percent 0.07 1.50 0.30 0.65
Excellent quality welds for welding heavy sections of fine grained high strength steels with particular reference to low temperature service down  to minus 60⁰C. Typical applications include welding of Q&T Steels for pressure vessels, tanks, penstocks, where high strength  and sub-zero temperature toughness are of importance.
E9018
Element C Mn

Si Ni Mo
Percent 0.065 1.2 0.40 1.2 0.5
A low hydrogen, iron powder type electrode  for welding  steels having tensile strength upto 70kgf/mm^2. Ideally suited for  welding fine grained steels, high tensile steels in bridges, penstocks , tanks etc.
E10018-D2
Element C Mn Si Mo
Percent 0.06 1.85 0.45 0.40
A basic coated low hydrogen iron powder type electrode for welding high tensile steels. The metal is of radiographic quality. Ideally suited for welding high tensile steels, Q&T Steels, castings etc.
E11018-G
Element C Mn Si Mo Ni Cr
Percent 0.06 1.4 0.25 0.5 2.2 0.2
E11018 is a  low hydrogen type electrode ideally suited for welding high strength steels, fine grained steels, HSLA, Q&T Steels etc.
 
 
Welding Electrodes : Stainless Steel
Grade Characteristic
E308
Element C Mn Si Cr Ni
Percent 0.05 1.40 0.40 19.5 9.50
The weld metal displays good resistance to cracking, corrosion, and scaling. Ideally suited for welding stainless steel materials of similar composition like AISI 301, 302, 304, 308 etc.
E308L
Element C Mn Si Cr Ni
Percent 0.03 1.40 0.40 19.8 10
The weld metal has higher resistance to cracking, oxidation and scaling at elevated temperatures. Ideally suited for welding stainless steels of similar composition like AISI 304L, 308L and their equivalents for overlays, surfacing applications etc.
E308H
Element C Mn Si Cr Ni
Percent 0.06 1.40 0.40 19.5 10
The weld metal possesses excellent crack resistance and displays good elevated temperature properties. Ideally suited for joining 18/8 stainless steels where
E309
Element C Mn Si Cr Ni
Percent 0.06 1.80 0.50 23.5 12.5
The 309 electrode producing high strength stainless steel weld metal having good oxidation resistance upto 1100⁰C. The weld metal possesses excellent resistance to corrosion and oxidation. Ideal for welding 18/8 type steels to mild steel, clad side of 18/8 clad steels, lining of 12 Cr steels on mild steels, overlays of ferritic steels, dissimilar steels and difficult to weld steels.
E309L
Element C Mn Si Cr Ni
Percent 0.03 1.60 0.50 23.6 12.8
E309L is a stainless steel electrode depositing extra low carbon weld metal. The weld metal has excellent mechanical properties and possesses good oxidation and scaling resistance at elevated temperatures. Ideally suited for welding stainless steels, wrought and cast materials of similar composition, welding of 18/8 type stainless steel to carbon steel for buffer layers etc.
E309Cb
Element C Mn Si Cr Ni Cb
Percent 0.07 1.50 0.50 23.5 13 0.8
E309Cb is a stainless steel electrode depositing a columbium stabilized weld metal. Ideally suited for welding stabilized and unstabilised steels to mild steels.
E309Mo
Element C Mn Si Cr Ni Mo
Percent 0.05 1.80 0.50 23.5 13 2.4
E309Mo is a stainless steel electrode yielding a weld deposit of 25Cr-12Ni-2.5Mo, which has good oxidation resistance upto 1050⁰C. Ideally suited for welding 18-11 Mo type steels to mild steel.
E310

Element C Mn Si Cr Ni
Percent 0.17 2.40 0.50 25.8 21
E310 is a stainless steel electrode for welding steels of similar composition. The weld metal has excellent resistance to oxidation and scaling  upto 1200⁰C. The electrode is also suitable for welding of hardenable steels, clad steels, C-Mo, Cr-Mo steels where pre-heat and post weld heat treatment are not feasible.
E312

Element C Mn Si C Ni S P
Percent 0.08 1.4 0.55 28.8 10.1 0.012 0.025
E312 is a rutile type electrode which can be considered as outstanding by virtue of its excellent performance, characteristics and weld metal of controlled chemical composition. The weld metal is highly resistant to cracks and fissures. The typical application includes welding dissimilar metals, unknown metals, leaf and coil springs, gear teeth, forged shafts, earth moving equipment, and machine parts. Applications should be limited to service temperature below 420⁰C to avoid formation of secondary brittle phase.
E316

Element C Mn Si Cr Ni Mo
Percent 0.05 1.25 0.45 18.8 12 2.3
The weld metal displays good crack resistance, excellent creep strength and resists scaling at elevated temperatures up to 850⁰C. The weld metal has excellent resistance to corrosion and pitting.
E316L

Element C Mn Si Cr Ni Mo
Percent 0.035 1.75 0.45 18.5 12.5 2.3
The weld metal has excellent resistance to intergranular corrosion even at elevated temperatures. Ideally suited for welding stainless steels of similar composition.
E317L

Element C Mn Si Cr Ni Mo
Percent 0.035 1.60 0.46 19 12.2 3.2
E317L is a stainless steel electrode depositing an extra low weld metal containing 18Cr-12Ni-3Mo.
E318

Element C Mn Si Cr Ni Mo Cb
Percent 0.05 1.50 0.42 18.5 12 2.3 0.6
E318 is a stainless steel electrode producing a columbium stabilized weld metal. The weld metal produces a good resistance to corrosion and pitting and improved creep strength.
E347

Element C Mn Si Cr Ni Cb
Percent 0.05 1.40 0.45 19 10 0.60
Ideal for welding of AISI 304, 304L, 321, 347 and their equivalents. The weld metal as excellent resistance to intergranular corrosion.
E383

Element C Mn Si Cr Ni Mo Cu
Percent 0.03 1.50 0.90 27.7 31.5 3.7 1
E383 is a special electrode producing a  low carbon fully austenitic weld metal which exhibits  excellent resistance to corrosion in non-oxidising media like sulfuric acid, Phosphoric acid etc. Ideally suited for welding steels of similar composition and other equivalent grades.
E410

Element C Mn Si Cr Ni
Percent 0.07 0.8 0.6 12.5 0.35
Ideally suited for joining similar alloys, resurfacing of valve seats, steam and gas turbine components. Ideal for joining straight chromium stainless steels.
E430

Element C Mn Si Cr Ni
Percent 0.075 0.60 0.50 17 0.35
The weld deposit displays good resistance to corrosion and heat. The electrode is suitable for joining stainless steels of similar composition. It is also suitable for surfacing carbon steels, low alloy steels, and chromium steels. Typical applications include surfacing of valves, Impellers, turbine blades etc.
E2209
Element C Mn Si Cr Ni Mo N
Percent 0.035 1.50 0.4 22 9.4 2.9 0.14
E2209 is a specially formulated electrode depositing a stainless steel weld metal and is ideal for welding duplex stainless steels. The weld metal possesses excellent corrosion resistance in marine environments.
 
 
Welding Electrodes : Nickel based
Grade Characteristic
ENiCrFe2
Element C Mn Si Cr Ni Mo Fe Cb
Percent 0.04 2.5 0.4 15 Bal 1.5 7 1.5
It is a high Nickel alloy electrode suited for welding  of NiCrFe alloy to themselves, welding of dissimilar metals such as carbon steels, stainless steels , nickel based alloys and pure nickel to themselves or to each  other  for overlaying  applications.
ENiCrFe3
Element C Mn Si Cr Ni Mo Fe Cb
Percent 0.04 6 0.45 15 Bal 1.5 6 1.3
ENiCrFe3 is a basic coated electrode which deposits an inconel type weld metal. The electrode is specially suited for welding of 9% nickel steels , joining dissimilar metals, joining of  Ni-Cr-Fe alloy to themselves and  to dissimilar materials, cladding  and surfacing of parts subjected to corrosion and heat. The weld metal possesses excellent high temperature as well as sub-zero temperature properties.
ENiCrMo6
Element C Mn Fe P S Si Cu Ni
Percent 0.08 2.8 8 0.02 0.02 0.45 0.3 66
Element Cr Cb+Ta Mo W
Percent 13 1.5 6 1.5
The weld metal displays a good combination  of strength and impact strength  even at minus 196⁰C.Typical specification  of the weld metal which can be welded  with this electrode  are ASTMA 333, A334, A353, A522, & A553 etc.
ENi-1
Element C Mn Si Ni Fe T Al
ercent 0.04 0.6 0.5 Bal 0.6 2 0.6
ENi-1 is a basic coated electrode depositing a pure Nickel weld metal, ideally suited for welding wrought  and cast of commercially pure nickel to themselves, welding nickel to carbon steels, overlays on steel to resist corrosion in caustic soda service and marine atmosphere.
ENiMo-1
Element C Mn Si Cr Ni Mo Fe V
Percent 0.05 0.6 0.5 0.65 Bal 28 5 0.4
Element Co W P S
Percent 2 0.8 0.025 0.02
The weld deposit has excellent heat resistance, high strength upto 540⁰C and good corrosion resistance. Ideal for welding Ni-Mo alloys as well as the clad side of joints in steel clad with a Ni-Mo alloy  and for welding of Ni-Mo alloys to steel and to other nickel base alloys.
ENiCu-7
Element C Mn Si Ni Al Ti Fe Cu
Percent 0.05 2.8 0.5 66 0.6 0.6 1.3 Bal
ENiCu-7 is a basic coated electrode depositing monel weld metal. Ideal for welding of monel to monel, Ni-Cu alloys to themselves, Ni-Cu alloys to steels, for welding clad side of Ni-Cu clad steel and for surfacing on steel parts for service against corrosion by  sea water, chlorinated solvents, sulphuric acid and alkalies. Ideal for marine, chemical, food, dairy, and oil refining industries.
 
 
Welding Electrodes : Hard facing
Grade Characteristic
ECoCr-A
Ele C Mn Si Cr Ni Mo W Co Fe
% 1.2 0.63 0.95 29 2.7 0.04 4 Bal 2.3
ECoCr-A is a cobalt based electrode depositing a weld metal having 28Cr-5W-1C. The weld metal possesses excellent resistance to oxidation, impact, corrosion and heat. Its applications include overlay, surfacing applications which require heat resistance, oxidation resistance in combination with impact and mild abrasion.
ECoCr-B
Ele C Mn Si Cr Ni Mo W Co Fe
% 1.4 1 1.05 31 2.7 0.08 8.2 Bal 3.2
The weld metal possesses excellent resistance to oxidation, impact, corrosion and heat. Its application includes hard surfacing of valve seats, forging dyes, crushers, hummer edges, cutting knives and blowers etc.
ECoCr-C
Ele C Mn Si Cr Ni Mo W Co Fe
% 2.23 0.7 0.87 31 2.7 0.05 12.65 Bal 3.5
The weld metal possesses excellent resistance to oxidation, impact, corrosion and heat. Its applications include hard surfacing of valve heads, sealing rings of high pressure pumps and parts of crusher etc.
 
 
Welding Electrodes : Cast Iron
Grade Characteristic
ENiCuB
Element C Mn Si Ni Fe Cu
Percent 0.42 1.0 0.6 64 3.5 Bal
ENiCuB is a nickel copper alloy depositing a monel weld metal for welding of Cast Irons. The weld metal bonds easily with the cast iron. Ideal for repairing  defects in the foundary cast iron castings, repairing  of cracks, broken parts  of cast iron etc.
ENiCI
Element C Mn Si Ni Fe
Percent 0.8 0.15 0.8 Bal 4
ENiCI is an electrode depositing high nickel weld metal for welding of cast irons. The deposit is soft and has good resistance to cracking. Ideally suited for welding of cast iron to produce machinable
weld deposit.
ENiFeCI
Element C Mn Si Ni Fe
Percent 0.9 0.70 0.9 54 Bal
ENiFeCI is an electrode depositing a ferro nickel alloy weld metal, ideal for welding of several types of cast iron and components for producing strong crack free weld joints. The weld deposit has good machinability and color match with parental metal.
 
 
Home | About Us | Products | Mild Steel | Low Alloys | Stainless Steel | Nickel Alloys | Enquire Now | Contact Us
Caston Electrode Company : 6 / 5, Didar House Building, DLF Industrial Area, Moti Nagar New Delhi-110015 (India) Ph.:+91-11-42352200